The experiment of hot dip interaction tests was carried out in order to study the formation behavior of interfacial reaction layer between as-received STD61 hot work tool steel and a commercial pure aluminum melt, Al-xwt.%Fe(x=0.2, 0.5, 0.8 and 1.1) alloys melt and Al-xwt.%Si(x=1.0, 4.0, 7.0 and 10.0) alloys melt, respectively. The results show that the reaction layer, over 300 ${mu}m$ in thickness, is easily formed by the dissolution of silicon from as-received tool steel. When the iron content in the aluminum alloy is higher than 1.1 wt.%, the thickness of reaction layer decreases below 180 ${mu}m$ by preventing iron dissolution from the tool steel. The silicon dissolved from tool steel acts as a strong promoter on the formation of reaction layer, but the alloyed silicon in molten aluminum alloys acts as an inhibitor on the formation of reaction layer.