Titanium and Titanium alloys are widely used as an orthopedic and dental implant material because of their excellent biocompatibility and mechanical strength. In this study, ECAP Cp-Ti and Cp-Ti were heat treated for different annealing time of 30 min, 90 min and 3 hours. The grain size for each condition was studied. The micro-Vicker hardness test was carried out f3r each different heat treated samples. The micro-Vicker hardness test for ECAP Cp-Ti, Cp-Ti and Cp-Ti (3hr) revealed hardness values of 239.5, 182 and 144 Hv, respectively. The grain size was increased from approximately $70{mu}m;to;300{mu}m$ with the increase in heat treatment time from 30 min to 3 hours. The heat treated samples were tested for their biocompatibility in simulated body fluid (SBF) and corrosion rates was determined using Polarization Curve test (PCT). The PCT results showed Cp-Ti with comparatively high corrosion potential of -0.18 V and corresponding corrosion current of $2 imes10^{-6}$ A, while the corrosion rate in ECAP Cp-Ti and Cp-Ti (30 min annealed) showed very similar results of corrosion potential about -0.47 V with corresponding corrosion current of $7 imes10^{-8}$ A.