In order to reduce the weight of glass in architecture, automobile, bottles, displays, a new technique that can strengthen glass was developed using various method. Generally, the strength achieved of glass-ceramics is higher as is 1.he fracture toughness by the formation of a crystalline phase inside glass. In this study, $70SiO_2-20Na_2O-10CaO-10TiO_2$ glasses were irradiated to strengthen by heterogeneous phase using femto-second laser pulse. Laser pulse irradiation of samples was analyzed by DTA, TMA, XRD, nano-indenter and SEM. Samples irradiated by laser had lower value$(3~4 imes10^{-3}Pa)$ of nano indentation which related with mother glass$(8 imes10-3Pa)$ than values. Microcracks were occurred around laser irradiation area when femtosecond laser with the repetition rate of 1kHz was used as the light source to induced heterogeneous phase.