In this study, in order to develop low temperature sintering ceramics for ultrasonic vibrator application, PNW-PMN-PZT system ceramics were manufactured according to the amount of CaCO$_3$ addition, and their piezoelectric, dielectric and microstructural characteristics were investigated. The ceramic specimens could be sintered at sintering temperature below 1000 $^{circ}C$ due to the effect of Li$_2$CO$_3$-CaCO$_3$ liquid phase produced by the reaction of Li$_2$CO$_3$ and CaCO$_3$. At 0.2 wt% Li$_2$CO$_3$ and 0.25 wt％ CaCO$_3$ added specimen sintered at 920 $^{circ}C$, the density, electromechanical coupling factor(k$_{p}$), mechanical quality factor(Q$_{m}$) and dielectric constant showed the optimal value of 7.78 g/㎤, 0.49, 1396, and 1300, respectively, for ultrasonic vibrator application.ion.???????????6??K?乍??????????