YBCO coated conductors have been fabricated with a newly developed oxide-precursor-based MOD process. The precursor solution was synthesized with low cost YBCO powders as starting materials and YBCO coated conductors have been deposited on IBAD substrate ($CeO_2$/IBAD-YSZ/SS). YBCO coated conductor prepared by dip coating shows transport $I_c$ of $15 A/{cal}cm-w at 77 K. Microstructural and crystallographic analyses indicate that YBCO layer was grown in epitaxy with substrate and exhibited well-developed dense microstructure. Also discussed are processing and analysis of YBCO coated conductor by slot-die web coating method. It was shown that this oxide-based MOD process provides a low cost route to coated conductor with high $J_c$