The corrosion experiment was performed for 120 hours on the specimens in the natural seawater tank with four steps of the loaded torsional stress. The surface corrosion pattern of SCM440 area was showed global corrosion and narrow pitting, that was cause by galvanic corrosion between friction welded IN713LC and SCM440. But corrosion does not proceeded from IN713LC area. Initially, the average relative electrode potential and corrosion current were decreased suddenly, by and large, it was stabilized gradually tend to decreasing with the elapse of the immersion time. The corrosion rate was decreased by increasing the load stress, but 200 MPa specimen was showed most large value.