High-quality single crystals of pure $Li_2B_4O_7$ as well as $Li_2B_4O_7$ doped with Cu, Mn and Mg impurities (1.0mol%, respectively) have been grown from the melt of $Li_2CO_3+2B_2O_3$ by Czochralski method in platinum crucibles. To study the thermoluminescent properties, $Li_2B_4O_7$ series single crystal TLDs were made by cutting in the size of $4{ imes}5{ imes}1;mm^3$. The glow curves show two or three peaks which can be easily deconvoluted. It is observed that room temperature($20{sim}30^{circ}C$) fadings of the dosimetric peaks of $Li_2B_4O_7$ series single crystal TLDs were about 10 % for 30 days. The relative photon energy response for $Li_2B_4O_7$ series single crystal TLDs were about 85 % when the responses were normalized to that measured with $^{60}Co;(1.25;MeV);{gamma}-rays$. The measured data are in a good agreement with theoretical ones. The $Li_2B_4O_7$ series single crystal TLDs fabricated in this work can be used for monitoring personal and environmental radioactivity.