Conducting polymer (Polypyrrole) and Tin oxide ($SnO_{2}$) composite films have been fabricated with layer-by-layer technique. $SnO_{2}$ layer was screen-printed on $Al_{2}O_{3}$ substrate and then was dip-coated with polypyrrole (Ppy). The microstructures of composite films were evaluated by a field emission scanning electron microscope (FE-SEM) and FTIR spectral analysis. The change in sensitivity to various VOCs was observed. The target VOCs were methanol, ethanol, benzene and toluene. The sensitivities of the $Ppy/SnO_{2}$ sensor to benzene and toluene were very low at 1000 ppm (2.1 %, 1.5 %), while the sensitivities to methanol and ethanol was high (9 %, 11 %). It indicates that the sensors have selectivity to alcoholic gases such as methanol and ethanol.