Dense $0.95(Na_{0.5}K_{0.5})NbO_3-0.05LiTaO_3$ (NKN-5LT) ceramics were developed by conventional sintering process. Sintering temperature was lowered by adding $Na_2CO_3$ as a sintering aid. The electrical properties of NKN-5LT ceramics were investigated as a function of $Na_2CO_3$ concentration. When the sample sintered at $1000^{circ}C$ for 4 h with the addition of 1 mol% $Na_2CO_3$, electro-mechanical coupling factor $(k_p)$ and piezoelectric coefficient $(d_{33})$ of NKN-5LT ceramics were found to reach the highest values of 0.43 and 190 pC/N, respectively.