Statement of problem: Modification of titanium implant surface has potential to ensure clinically favorable performance that several surface modification technologies have been introduced. Among the methods. anodizing method and sol-gel hydroxyapatite coating method have gained much interest due to its roughness and chemical composition of the coating layer, but more of its biocompatibility result is required. Purpose : The purpose of this study was to compare bone-implant interface shear strength of four different surface treated implants as time elapsed. Resonance frequency analysis(RFA) and removal torque measurement methods were employed to measure implant stability at one week and six week after implantation. Material and method: A total of 80 screw-shaped implant [20 machined, 20 resorbable media blasted(RBM), 20 anodized, and 20 anodized+hydroxyapatite sol-gel coated] were prepared, and one of each group was implanted in the tibia of a New Zealand white rabbit that total 20 of them were used. In order to test the implant stability and implant-tissue interface contact changing in the bone bed, each 10 rabbit were sacrificed 1 week and 6 week later while resonance frequency and removal torque were measured. One-way analysis of variance and the Tukey test were used for statistical analysis. Results : The results were as follows. 1. There was no statistically significant difference of implant stability quotients(ISQ) value in RFA between individual groups after 1 week of implantation and 6 weeks(p>0.05). But, there was statistically significant increase of ISQ value in 6 weeks group compared to 1 week group(p<0.05). 2. There was no statistically significant difference in removal torque analysis between individual groups after 1 week of implantation and 6 weeks(p>0.05). but there was statistically significant increase in all 4 groups after 6 weeks compared to 1 week later(p<0.05). 3. There was no statistically significant difference in removal torque analysis between anodized group and HA coating after anodic oxidation 6 weeks later(p>0.05), but significant difference was appeared in both groups compared to RBM group and smooth-machined group(p<0.05). Conclusions : It can be suggested that changes in surface characteristics affect bone reactions. Anodized and anodized+hydroxyapatite sol-gel coating showed significantly improved bone tissue response to implants, but further study on the effect of hydroxyapatite dissolution is needed.