The effects of Ba and Ce addition has been investigated in YBCO prepared by trifluoroacetate(TFA) metalorganic depostition(MOD) method. Precursor solutions with cation ratios of Y:Ba:Cu:Ce=1:2+x:3:x(x=0, 0.05, 0.1 and 1.5) have been prepared by adding an excess amount of cerium and barium. Coated film was calcined at lower temperature under a moisture-containing oxygen atmosphere. Superconducting YBCO films have been obtained by performing conversion heat treatment at temperature of $780{sim}810^{circ}C$ under a moisture-containing Ar(1,000 ppm oxygen) atmosphere. It has been shown that the critical current($I_c$) of YBCO film was degraded by doping of Ba and Ce atoms. But $I_c$ was increased as the amount of doped Ba and Ce content increased from 5% to 15 %. It was observed that there was little increase of a flux pinning force with Ba and Ce addition in YBCO film prepared by TFA-MOD process.