[$Bi_2Sr_2Ca_1Cu_2O_x$](BSCCO 2212) tubes were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted in a Pt crucible and solidified in a rotating steel mold. The BSCCO 2212 tube samples separated from steel mold were heat-treated at $800^{circ}C;and;810^{circ}C$ in oxygen flow. The critical current($I_c$) of the samples was measured by transport measurement at 77K, and the microstructure was investigated by scanning electron microscope. The $J_c$ at 77K of the tubes heated treated at $800^{circ}C;and;810^{circ}C$ were 197 and 240 $A/cm^2$, respectively. It was observed that the plate like grains in BSCCO 2212 tube was more developed in the sample heat treated at $810^{circ}C;and;800^{circ}C$ heated tube. It is found that the critical current($I_c$) of the BSCCO 2212 sample was dependent on the heating schedule regarding the growth of the BSCCO 2212 grains.