We studied the mechanical and magnetic properties of Y-Ba-Cu-O superconductor with and without resin and Ag impregnation. Bulk YBCO superconductor was manufactured with the top-seeded melt-growth method. Typical sample of 40mm X 20mm X 3mm was made and then 8 holes with 0.5mm diameter were drilled arbitrally. Epoxy resin and $AgNO_3$ were systematically added into the holes to compare the mechanical and magnetic properties of YBCO superconductor before and after reinforcement of resin and Ag. Based on the result of 3 point bending, bending strength increased with increasing amounts of resin and carbon nano-tube. However, it was found that the levitation force decreased after making hole, compared with virgin sample without hole.