Biaxially textured Ni was fabricated by electrodeposition process and delaminated from the biaxially textured cathode surface for further buffer layer deposition process. Those electrode posited Ni substrates showed well-developed biaxial texture and smooth surface. In order to improve the thermal stability of Ni substrates, Mn was alloyed by adding Mn precursor into the electrodeposition bath. Subsequently, $CeO_2$ buffer layers are deposited by MOD process to prevent interfacial reaction between superconductor and substrates. In particular, Bismuth oxide was added to $CeO_2$ to realize lower temperature processing of buffer layers. The microstructure and texture development of each layers have been investigated. Preliminary results shows that all electro/chemical process can be a candidate for cost effective route to YBCO coated conductor.