The microstructures and mechanical properties of continuously porous $SiC-Si_3N_4$composites fabricated by multi-pass extrusion were investigated at different Si levels added. Si-powder with different weight percentages (0%, 5%, 10%, 15%, 20%) was added to the SiC powder to make the raw mixture powders, with $6wt%Y_2O_3-2wt%Al_2O_3$ as sintering additives, carbon ($10-15{mu}m$) as a pore-forming agent, ethylene vinyl acetate as a binder and stearic acid ($CH_3(CH_2)_{16}COOH$) as a lubricant. In the continuously porous $SiC-Si_3N_4$ composites, $Si_3N_4$ whiskers like the hairs of nostrils were frequently observed on the wall of the pores. In this study, the morphology of the $Si_3N_4$ whiskers was investigated with the silicon addition content. In the composites containing of 10 wt% Si, a large number of $Si_3N_4$ whiskers was found at the continuous pore regions. In the sample to which 15 wt% Si powder was added, maximum values of about 101 MPa bending strength and 57.5% relative density were obtained.