The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, the effect of shot peening in corrosion environment was not known. In this study, investigated is the effect of shot peening on corrosion fatigue crack growth of SAE 5155 steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of SAE 5155 are as follows; the fatigue crack growth rate of the shot peening material was lower than that of the non-peening material. And fatigue life shows more improvement in the shot peening material than in non-peening material. This is due to the compressive residual stress of surface increases resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.