In the present study, the possibility of Mg-Zn-Y alloys as high temperature casting alloys has been investigated. The fluidity of alloys containing yttrium were better than that of commercial AZ91 alloy because the oxide layer on the surface reduced the reaction between melt, and air and mold, which would reduce the resistance during the process of filling the mold. However, this oxide film reduced the hot-tearing resistance. In the case of ZAW942, this alloy exhibited fluidity and hot-tearing resistance better than AZ91 alloy. Because of thermally stable quasicrystal and other phases obstructed the movement of grains, the creep resistance of alloys containing rare earth elements more than 2 wt% was better than that of AZ91 alloy.