Sr, added in the hypereutectic Al-Si alloys, is absorbed on the surfaces of primary Si as well as eutectic Si, and can change the growth mode of primary Si from non-faceted to faceted mode, as the amount of Sr increases larger than 0.04 wt.%, even though it cannot affect the grain size of primary Si, significantly. The EBSD analysis shows that the traction of ${Sigma}3$ boundary(twin boundary) increases as the amount of Sr in the hypereutectic Al-Si alloys increase until the over-modification occurs at 1.6 wt.%Sr and proves that the change in growth mode of primary Si results from the change of TPRE growth to IIT growth.