The effect of A/B moi ratios and sintering temperatures on dielectric properties and microstructure of $(Ba_{0.93}Ca_{0.07})_m(Ti_{0.82}Zr_{0.18})O_3$ ceramics were investigated. The dielectric constant decreased with increasing the A/B mol ratio. However, the dielectric loss is improved. As the dielectric properties of A/B mol ratio with m = 1.009 at sintered temperature $1260^{circ}C$, we obtained dielectric constant 12,800, dielectric loss $3.5\%$ and Y5V temperature characteristics. Highly reliable Ni-MLCCs, 1.6mm$(length){ ime}0.8mm(width){ ime}0.8mm$(height) with capacitance of 1.23 ${mu}F$ and 야ssipation loss of $5.2\%$ were obtained employing dielectric material composed of $(Ba_{0.93}Ca_{0.07})_{1.009}(Ti_{0.82}Zr_{0.18})O_3$ - $MnO_2;0.2wt\%-Y_2O_3;0.18wt\%,;-;SO_2;0.15wt\%-(Ba_{0.4}Ca_{0.6})SiO_3;1wt\%.$