In this study, systematical investigations were carried out on crystal qualifies and optical properties of $ZnSe_{1-x}:Te_x$ (x=0.002-0.04) thin films frown by molecular beam epitaxy (MBE). The crystal qualifies and optical properties have been investigated by X-ray diffraction (XRD) and Photoluminescence (PL) measurements, respectively. From the XRD measurements, the crystallographic characteristics showed mediocre crystal quality with increasing the Te composition. From the PL measurements, emission in the visible spectrum region from blue to green was obtained by varying the Te content of the ZnSe:Te epilayers. The efficient blue and green emission were attributed to the recombination of excitons trapped at isoelectronic isolated a single Te atom and $Te_n(n{geq}2)$ clusters. respectively. The blue emission become dominant in Te tightly doped $ZnSe_{1-x}:Te_x$ $(Te=0.2\%)$ epilayers with increasing temperature. For the Te heavily doping condition $(Te=4.0\%)$, the dominant green emission could be observed at around 160K.