[ $LiFePO_4$ ] is one of the promising materials for cathode material of secondary lithium batteries due to its high energy density, low cost, environmental friendliness and safety. $LiFePO_4$ was synthesized by the solid-state reaction method at 500 - 800°C. The crystal structure of $LiFePO_4$ was analyzed by X-ray powder diffraction. The samples synthesized at 600 and $700^{circ}C$ showed a single phase of a olivine structure. The particle sizes were increased and the specific surface areas were decreased with heating temperatures. The electrochemical performance was investigated by coin cell test. The discharge capacities at 0.1 C-rate were 118 mAh/g and 112 mAh/g at $600^{circ}C,;700^{circ}C$, respectively. In an attempt to improve the electrical conductivity of cathode materials, $LiFePO_4/graphite$ composite was prepared with various graphite contents. The electrical conductivity and discharge capacity were increased with increasing the graphite contents in composite samples. The rate capabilities at high current densities were also improved.