Optimization of process variables, including oxygen and water partial pressure and also an nesting temperature, was performed in batch-type process to fabricate YBCO films on LaAlO3 single crystal. In this work, YBCO oxide powder was used as a starting precursor for metal-organic deposition(MOD)method. The precursor films were fabricated in batch furnace and they were converted to the epitaxial YBCO films at the same furnace with varying the process variables. The oxygen partial pressure was varied from 100ppm to 2000ppm and the water partial pressure from 1.2% to 12.2%. The window for optimal P(O2) was narrow about 700ppm for batch-type process. YBCO films in bathc-thype MOD process were optimized at 740-770oC and P(H2O) of 2.3%-7.3%.