To research of the improved mechanical properties of materials for spectacle lens cutting, SiC and TiC were used as the main powder. Also, $Al_2O_3$ and $Y_2O_3$ was included as a sintering additive. The weight ratio of the alumina($Al_2O_3$) to yttria($Y_2O_3$) was set to 1:1. The materials for spectacle lens cutting were fabricated by hot-pressing at $1810^{circ}C$ for 1h and subsequently annealed at $1860^{circ}C$ for 3, 6 and 12h to initiated grain growth. The longer annealing time is, the bigger the grain size is. The microstructures were observed by scanning electron microscopy (SEM). The SEM images were quantitatively analyzed by image analysis (Image-Pro Plus, Media Cybernetics, Maryland, U.S.A.). Crack deflection by elongated SiC grains was most frequently observed as the dominant toughening mechanism. Crack deflection was generally observed for elongated SiC grains with aspect ratio(AR) > 2.5 and grain thickness < $2.3{mu}m$. Crack bridging was also observed as one of the operating toughness mechanism.