Highly ordered Li dispersed nickel oxide nanotubes were prepared with anodic aluminum oxide (AAO) template for hydrogen storage. Electron microscope results showed that uniform length and diameter of nickel oxide nanotubes were obtained. The wall thickness and outer diameter of nickel oxide nanotubes are about 40 - 50 nm and 200 - 400 nm, respectively. It was observed that the diameter of nickel oxide nanotubes is bigger than the pore diameter of AAO template. Li dispersed nickel oxide were consisted of nanoflakes and had structures of nanotubes and nanorods. For increasing the hydrogen adsorption and desorption capacity, the Li dispersed nickel oxide nanotubes were fluorinated. The fluorinated Li dispersed nickel oxide nanotubes showed 1.65 wt% of the hydrogen adsorption capacities at 77 K under 47 atm.