By calcining at $750^{circ}C$ for 30 h in $O_2$ stream after milling, $LiNi_{1-y}In_yO_2$(y = 0.005, 0.01, 0.025, 0.05, and 0.1) were synthesized and their electrochemical properties were investigated. All the samples had the $R{ar{3}}m$ structure. In addition, they contained $LiInO_2$ phase and the intensities of the peaks for the $LiInO_2$ phase increased as the value of y increased. The sample with y = 0.01 had the largest first discharge capacity (140.2 mAh/g), but the sample with y = 0.005 had a better cycling performance. The samples with y $geq$ 0.025 had a bad cycling performance irrespective of the first discharge capacity. The sample with y = 0.005 had the largest value of $I_{003}/I_{104}$ and the smallest value of R-factor. Among all the samples, $LiNi0_{0.995}In_{0.005}O_2$ had the best electrochemical properties. This sample had a smaller first discharge capacity than $LiNiO_2$, but it showed a better cycling performance than $LiNiO_2$.