The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper, and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The $60^{circ}$ specular gloss, impact resistance, cross-hatch adhesion, and heat resistance of the films proved to be good, and the pencil hardness, drying time, and pot-life proved to be slightly poor. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value.