White polymeric light-emitting devices (WPLEDs) have been fabricated from polyfluorene-based (PFO) blue and MEH-PPV polymer blending systems. A device structure of ITO / PEDOT:PSS / Blending polymer / Blue polymer / LiF / Al was employed. This structure of double emission layers showed significant improvement of white color shift phenomenon. A current efficiency of 4.67 cd/A (3,900 $cd/m^{2}$, 6.4 V) and a brightness value of 17,600 $cd/m^{2}$ at 9.4 V with (0.34, 0.35) CIE coordinates at 5 V and (0.29, 0.29) at 9 V were achieved achieved.