The effect of the processing parameters on the sintered density and strength of silica-bonded SiC (SBSC) ceramics was investigated for three types of batches with different particle sizes. The SBSC ceramics were fabricated by an oxidation-bonding process. The process involves the sintering of powder compacts in air so that the SiC particles bond to each other by oxidation-derived $SiO_2$ glass or cristobalite. A finding of this study was that a higher flexural strength was obtained when the starting powder was smaller. When a ${sim}0.3_{-{mu}m}$ SiC powder was used as a starting powder, a high strength of $257{pm}42;MPa$ was achieved at a relative density of ${sim}80%$.