We report on the fabrication of organic-based flexible displays using an amorphous IZO anode grown at room temperature. The IZO anode films were grown by a conventional DC reactive sputtering on the polycarbonate (PC) substrate at room temperature using a synthesized IZO target in a $Ar/O_2$ ambient. Both x-ray diffraction (XRD) and high resolution electron microscope (HREM) examination results show that the IZO anode film grown at room temperature Is complete amorphous structure due to low substrate temperature. A sheet resistance of $35.6Omega/Box$, average transmittance above 90 % in visible range, and root mean spare roughness of $6sim10.5AA$ were obtained even in the IZO anode film grown on PC substrate at room temperature. It is shown that the $Ir(ppy)_3$ doped flexible organic light emitting diode (OLED) fabricated on the IZO anode exhibit comparable current-voltage-luminance characteristics as well as external quantum efficiency and power efficiency to OLED fabricated on conventional ITO/Glass substrate. These findings indicate that the IZO anode film grown on PC substrate is a promising anode materials for the fabrication of organic based flexible displays.