In order to examine the working condition of melts in tin bath of float process it was investigated Sn diffusion behavior and solidification rate of melts for alkali-alkaline earth-silica PDP substrate glasses such as commercial CaO rich CS-77 glass, commercial $Al_2O_3$ rich PD-200 glass and self developed $SiO_2$ rich T-series (T-2, T-4, T-6) glasses. In the case of Sn depth and concentration created in glass surface by ion exchange between Sn and alkali, T-series showed lower value than CS-77, especially T-2 is more excellent than PD-200. The solidification rate of melts expressed by cooling time between $log{eta}=4;and;7.6dPa{cdot}s$ was low for T-series comparing with CS-77 and PD-200. Therefore, it was concluded that T-series is desirable considering forming condition in the tin bath of the float process.