A new $TiN-Ti_5Si_3$ bulk composite was synthesized from preceramic, inorganic polymer (methylpolysilsesquioxane) and $TiH_2$ filler powders via polymer pyrolysis. Using this process, ceramics with high melting points can be produced relatively easily to a near net shape. The $TiN-Ti_5Si_3$ composite oxidized slowly during heating to $1000^{circ}C$. During heating at the temperatures of at 700 and $800^{circ}C$, TiN oxidized to Rutile-$TiO_2$ whereas $Ti_5Si_3$ resisted to oxidation. The oxide scale formed consisted primarily of $TiO_2$ containing $Ti_5Si_3$.