This study investigates the influence of various blending factors on cement paste fluidity and find out the most effective evaluation method of cement paste flow, comparing flow test apparatuses such as ring flow(R-F), flow cone(F-C) and mini slump(M-S). A viscometer also measures the rheology coefficients to secure faithful numerical data. Firstly, series I examines cement paste, affected by several cement products and mineral admixture types in the range of W/B 40%, ordinary fluidity, and W/B 30%, high fluidity. In this series, the three types of cement product depended on companies, are randomly used and the mineral admixture, such as fly ash, blast furnace slag and silica fume, are incorporated in the cement paste, in response to the ratio of 10, 20, to 30%, respectively. In addition, series II studies various chemical admixture types, affecting the cement paste. This series is carried out with manufacturing companies and component types in the range of W/C 30%, high fluidity. For the manufacturing companies, randomly four products are used and for the component types, polycaboxylate, melamine, naphthalene and lignosulfonate type are chosen. Test results showed that in the fluidity test of cement paste considering various types of blending factors, R-F exhibited similar tendency with F-C and M-S. In the analysis of consistency curves measured by viscometer, the fluidity evaluation method using flow test apparatuses was significantly effective, except for the some of the low fluidity specimens. In conclusion of this study, R-F was the most convenient, faithful and effective fluidity evaluation method of cement paste.