To increase freeze-thaw resistance of porous concrete, this study examined physical properties of polymer by replacing paste used as a binding material with polymer, using unsaturated polyester and epoxy resin, and changing the mixing ratio of polymer. According to the result of this study, when the mixing ratio of resin paste to aggregates was 11 to 16%, voids volume was 33 to 37% and unit weight was about 1620 to 1720kg/$m^3$. In comparison with previous studies using cement paste, voids volume increased by about 7 to 16%, while unit weight decreased by about 100 to 300kg/$m^3$. Compressive strength was 90 to 155kg/$cm^2$ at the age of 7 days, which was 5-40kg/$cm^2$ bigger than porous concrete using cement paste. From a viewpoint of freeze-thaw resistance, it was identified that pluse velocity fell by 0.23km/sec, about 7% of the original velocity, when the cycle of freeze-thaw was repeated 300 times. In spite of 300 repetitions of the cycle, relative dynamic modulus of elasticity was more than 60%, which suggested that its freeze-thaw resistance was more excellent compared with the result that relative dynamic modulus of elasticity of porous concrete using cement paste was 60 % or less under the condition of 80 repetitions of freeze-thaw cycle.