Ceramic green sheets consisting Bi-based glass frit were fabricated for an application to PDP transparent dielectric front panel. The dispersion condition of the slurry for tape casting was pre-examined, and two kinds of hinder and plasticizer were used in the non-aqueous slurry system. In the fabrication process for the frit film, the properties such as dry and firing shrinkage, elongation, and transmittance were examined at the condition of various mixing ratio of plasticizers. In the mixing ratio of polyethylene glycol to dibutyl phthalate of 3:5wt%, a good adhesion, elongation and transmittance were observed at the firing temperature of $580^{circ}C$. The photograph for the cross section of the interface was also showed a dense microstructure.