In order to develop the composition ceramics capable of being sintered at low temperature with high piezoelectric properties for multilayer piezoelectric actuator application, PZW-PMN-PZT system ceramics were manufactured according to sintering aid $Li_2CO_3$ addition and their microstructural, dielectric and piezoelectric properties were investigated. The crystal structure of the specimens showed a perovskite phase and no pyrochlore or other second phase was detected. At the sintering temperature of $900;^{circ}C,;0.2;wt%Li_2CO_3$ added specimen showed a optimum values of kp = 0.562, $d_{33};=;360;pC/N$ and Qm = 1184, respectively.