We fabricated thin films of Au and Ta/Au with thicknesses of 30 nm and 5 nm/30nm, respectively on Si(100) or Si(111) substrates using a dc magnetron sputtering system. Grain sizes, roughness and conductivity for Au thin films are measured as a function of the annealing temperatures. We observed that the grain size of samples enlarged and the surface became rougher with increasing annealing temperature. The grain size and roughness were improved in the structure of Si/Ta/Au than Si/Au. Furthermore, the Si(100) substrate was more effective for decreasing the resistance for Ta/Au system than Si(111) substrate. We confirm that by inserting a Ta buffer layer in Si(100)/Au, surface roughness was reduced and by adjusting the annealing temperature the grain size were enlarged. Consequently, the Au thin-film has improved conductivity.