The high electrical conductivity Cu-0.15% Sn alloys containing various P contents, and the high conductivity and high strength Cu-0.1% Sn-0.1%Ag alloys with various Mg/P additions were fabricated and their mechanical properties and electrical conductivity were investigated. The electrical conductivity was generally decreased as the P content was increased where as the hardness and strength was shown to increase. When Mg was added to P-containing Cu alloys, the detrimental effect of P on the conductivity was significantly reduced, and TEM observations indicated that the formation of $Mg_3P_2$ phase is responsible for this result.