Dielectric and piezoelectric properties of $0.57Pb(Sc_{1/2}Nb_{1/2})O_{3}-0.43PbTiO_{3}$, which is the morphotropic phase boundary composition for the PSN-PT system, were investigated as a function of $Fe_{2}O_{3},;Nb_{2}O_{5};and;MnO_{2}$ addition 0 wt% to 0.9 wt%. The maximum dielectric constant of ${varepsilon}_{33}/{varepsilon}_{o}=2054$ and the minimum dielectric loss of $tan{delta}=0.37;%$ at room temperature were obtained at 0.1 wt% of $Fe_{2}O_{3}$ and 0.5 wt% of $MnO_{2}$ addition, respectively. With addition of 0.5 wt% $Nb_{2}O_{5}$ and $0.5;wt%;MnO_{2}$, the electromechanical coupling factor $k_{p}$ and mecanical quality factor $Q_{m}$ were significantly increased, respectively. The maximum electromechanical coupling factor $k_{p}=61.5;%$ was obtained by addition of $Nb_{2}O_{5}$ and high mechanical quality factor $Q_{m}=919$ was obtained by addition of $MnO_{2}$. The $Q_{m}(=919)$ value is 3.3 times larger than that of non-doped 0.57PSN-0.43PT ceramics.