Zinc gallate $(ZnGa_2O_4)$ thin film phosphors have been formed on ITO glass substrates by a sol-gel spinning coating method. For the formation of the film phosphors, the starting materials of zinc acetate dihydrate, gallium nitrate hydrate and 2-methoxyethanol as a solution were used. The thin films deposited were firstly dried at $100^{circ}C$ and fired at $500^{circ}C;or;600^{circ}C$ for 30 min and then, annealed $500^{circ}C;or;600^{circ}C$ at for 30 min under an annealing atmosphere of 3% $H_2/Ar$. The thin films deposited on ITO glass plates showed the (220), (222), (400), (422), (511), and (440) peaks of spinel structure as well as the (311) peak indicating a standard powder diffraction pattern. The surface morphologies of the thin film phosphors were observed with a firing and an annealing condition. The $ZnGa_2O_4$ film phosphors showed the blue emission spectra around 410 nm as well as the emission spectra in the UV region (360-380 nm).