Optimum compositions for piezoelectric properties of $(Bi_{0.5}Na_{0.5})_{(1-x)}Ba_xTiO_3$ ceramics were investigated in the range of $x=0{sim}0.1$ covering rhombohedral to tetragonal phase regions. No impurity phases other than a perovskite phase were found and the grain size decreased with increasing x. A two-phase coexisting morphotropic phase area rather than boundary dividing rhombohedral and tetragonal phase regions appeared to exist at $x=0.05{sim}0.08$. As for piezoelectric properties within morphotropic phase compositions, the piezoelectric constant ($d_{33}$) and the electromechanical coupling factor ($K_p$) showed peak values at x=0.065, 192 pC/N and 34%, respectively, indicating x=0.065 as an optimum composition for piezoelectric $(Bi_{0.5}Na_{0.5})_{(1-x)}Ba_xTiO_3$ ceramics.