This paper describes the results of electrical characteristics assessment for organic insulations of polyethylene(PE) series insulations and acrylonitrile butadiene styrene copolymer(ABS). In the experiment, 4 kinds of specimens by composition density were tested in relative permittivity, specific resistance and tracking duration. A WinDETA system and a tracking test set manufactured for this assessment were used to measure the dielectric parameters and tracking duration, respectively. In measuring the tracking duration, the time from testing voltage application to testing circuit breaking due to the tracking current was measured. As a result, dielectric dispersion was observed in measuring the relative permittivity of ABS. It was confirmed that the relative permittivity decreased with the density of the PE series insulations and it depends rather on the temperature than frequency. In most specimens, specific resistance exponentially decreased with frequency and the result for each specimen was almost similar. By the way, in the tracking test, all the PE series insulations showed more excellent performance than ABS and especially in the case of HDPE, its tracking withstand performance was the best.