The purpose of this study was to evaluate the effects of cyanate methacylate on the shear bond strengths to bovine dentin surfaces as a dentin primers. Seven experimental adhesives were made with different mass fraction of Isocyanatoetylme-thacrylate (IEM), 40wt% HEMA (Wako Pure Chemical Industries Osaka, Japan), 0.6% camphoroquinone, 0.4% amine and ethanol as balance dentin bonding agents (0, 2, 4, 6, 8, 10, 12%) were made and applied on the surface of bovine dentin specimens of 7 experimental groups. Shear bond strengths were measured using a universal testing machine (Instro 4466). To identify the ratio and modes of cohesive failures, microscopic examinationn was performed. The ultra-structure of resin tags were observed under scanning electron microscope. The results were as follows ; 1) A higher shear bond strengths (33.62 MPa) in group 8% of Cyanate methacrylate to dentin were found, but there were no statistically significancy between Groups (p > 0.05). 2) The higher ratio of cohesive failures mode in group 2, 6, an 10% could be seen than that in any other groups. 3) A shorter resin tags were observed in all experimental groups. This could be resulted that the preventing from the cyanate methacrylate penetrate into dentin owing to reacting it with dentin collagen. Therefore the resin tags were shorter in lengths. Whether the higher bonding strengths of dentin bonding agents can be affected was not been assured with statistic results. The results indicated that the relation between tensile strengths of the dentin adhesives to bovine dentin and resin tags formed into the dentin could not affected. The main reason of increasing the shear bond strength to bovine dentin in experimental groups could not be assured.