LSM powder material for an oxygen-electrode(anode) of High Temperature Steam Electrolysis (RISE) was synthesized by a Modified-Glycine nitrate process(GNP). Amount of nitric acid and its concentration was varied to find out an appropriate composition for the oxygen-electrode(anode). In order to optimize the amount of Glycine used as an oxidant of self-combustion process, the ratio of Glycine to Anion was varied. $La_{0.8}Sr_{0.2}MnO_3$, $La_{0.5}Sr_{0.5}MnO_3$, and $La_{0.2}Sr_{0.8}MnO_3$ were synthesized in this study. Those LSM were dried for overnight to remove moisture from the material at $110^{circ}C$ and were calcined 2 hours at $650^{circ}C$ and were sintered in a furnace for 5 hours at $1400^{circ}C$. Their structures, surface morphologies, surface areas, and weight changes were investigated with XRD, SEM, BET, and TG/DTA. The best perovskite phase for the oxygen-electrode of HTSE was obtained with $La_{0.8}Sr_{0.2}MnO_3$ formula in which 100 ml of 3M nitric acid was used in the preparation of its formula. The optimized ratio of Glycine to Anion was 2.