To investigate the characteristics of green light-emitting OLED device, C545T material with $Alq_3$ was doped in the OLED device of $ITO(1500)/2-TNATA(400{AA})/NPB(80{AA})/Alq_3:C545T(160{AA})/Alq_3(240{AA})/LiF(3{AA})/Al(2400{AA})$ structure, which was used as a activator at the respective concentration of 0.5 vol.%, 1 vol.%, 2 vol.% and 3 vol.%. It was observed from the experiments that the device efficiency firstly increased with the increase of C545T concentration and the maximum efficiency of 10.9 cd/A and 4.28 lm/W was obtained at C545T concentration of 1 vol.%, and then the device efficiency decreased as the C545T activator concentration increased above 2 vol.% contents, while the longest lifetime of over 750 hours was obtained at C545T concentration of 1 vol.%.