Magnetization loss of HTS wire is strongly dependent on the critical current density and the aspect ration of the HTS wire. This paper presents the magnetization loss of stacked BSCCO wire and stacked YBCO wires which had different critical current densities. Width of the BSCCO wire was 4mm and widths of two YBCO wires were 4mm and 8mm. Single wire, two stacked three stacked and four stacked wires were fabricated and tested. Ratio of magnetization loss of BSCCO wire to YBCO wire was presented at single wire. For stacked wire, ratio of magnetization loss of single wire to stacked wire was presented. Test results shows that magnetization losses of stacked wires were greater than that of single wire at large high magnetic field above critical magnetic field.