In order to prepare high-solid coatings, acrylic resins, HSCs [poly (EA/EMA/2-HEMA/CLA)] that contain 90% solid, were synthesized by copolymerization of ethyl acrylate (EA), ethyl methacrylate (EMA), 2-hydroxyethyl methacrylate (2-HEMA) and caprolactone acrylate (CLA). The high-solid coatings named as CHSCs (HSCs/HDI-trimer) were prepared by the curing reaction between the acrylic resins containing 90% solid contents and the isocyanates (HDI-trimer) curing agent room temperature. The curing behavior and various properties were examined on the film coated with the both high-solid coatings. The glass transition temperatures $(T_g)$ of CHSCs increased proportionally with increasing the predicted $T_g$ value by Fox equation, and had nothing to do with the solid contents. The prepared film showed good properties for $60^{circ}$ specular gloss, impact resistance, cross-hatch adhesion and heat resistance, and bad properties for pencil hardness, drying time, and pot-life. Among the film properties, the heat resistance was very excellent and could be explained by the introduction of functional monomers of CLA.