Crystallisation kinetics of the erbium doped soda-tellurite glasses were studied using the differential thermal analysis (DTA) and differential scanning calorimetery (DSC) techniques. The DTA curves in the temperature range of 350 K to 650 K were obtained from isochronal heating rates, chosen in the range of 2 to 20 K/min. DSC isothermal curves were used to calculate the fraction of crystals formed on reheating. The apparent activation energies for devitrification were derived by measuring the shifts in the values of $T_g$ and $T_x$ with heating rates, using the Kissinger method. The derived values of apparent activation energies for isochronal and isothermal methods varied in the range of $190-204;{pm};5;kJ;mol^{-1}$. The X-ray powder diffraction analysis of heat treated and transparent samples showed the presence of nano-scale size sodium-tellurite crystals. These crystallites were found to have a strong influence on the full width of half maxima of the transition in $Er^{3+}:;^4I_{13/2}{ ightarrow}^4I_{15/2}$, which extended from 70 nm in the vitreous materials to 132 nm in glass-ceramic materials.