Titanium dioxide ($TiO_2$) films were deposited by RF reactive magnetron sputtering on non-alkali glass and single crystal MgO (100) substrate at substrate temperature of $400^{circ}C$. Micro structures of $TiO_2$ films were investigated by XRD, FE-SEM, and Pole figure measurements. $TiO_2$ films deposited on glass substrate showed preferred orientation of anatase (101), whereas $TiO_2$ films deposited on the MgO single crystal substrate showed hetero-epitaxial anatase (100). $TiO_2$ film grown on MgO substrate showed higher photoctalytic activity than that of glass substrate.