[ 0-3PbTiO_3/P$ ](VDF/TrFE) nanocomposites thin films for passive pyroelectric infrared sensor have been fabricated by two-step spin coating technique. 65 wt% VDF and 35 wt% TrFE was formed to a P(VDF/TrFE) poder Nano size $PbTiO_3$ powder was used. 0-3 connectivity of $PbTiO_3$(VDF/TrFE) composites film is achieved and also observed by SEM photography successfully. The dielectric constant, and pyroelectric coefficient measured and compared with P (VDF/TrFE). A very low dielectric constant (13.48 at 1 kHz) and high enough pyroelectric coefficient (3.101 $nC/cm^2$.k at $50^{circ}C$) neasured. This nanocomposites can be used for a new pyroelectric infrared sensor for better performance.