Hafnium oxide $(HfO_2)$ films were deposited on Si(100) substrates by remote plasma-enhanced atomic layer deposition (PEALD) method at $250^{circ}C$ using TEMAH [tetrakis(ethylmethylamino)hafnium] and $O_2$ plasma. $(HfO_2)$ films showed a relatively low carbon contamination of about 3 at %. As-deposited and annealed $(HfO_2)$ films showed amorphous and randomly oriented polycrystalline structure. respectively. The interfacial layer of $(HfO_2)$ films deposited using remote PEALD was Hf silicate and its thickness increased with increasing annealing temperature. The hysteresis of $(HfO_2)$ films became lower and the flat band voltages shifted towards the positive direction after annealing. Post-annealing process significantly changed the physical, chemical, and electrical properties of $(HfO_2)$ films. $(HfO_2)$ films deposited by remote PEALD using TEMAH and $O_2$ plasma showed generally improved film qualities compare to those of the films deposited by conventional ALD.